Textiles with broad functionality are increasingly popular within the sports- and leisure industry. Athletes wear sports cloths with thermal regulative properties. That has commonly applied in many high-quality outdoor products.

Further sports-oriented textile areas are various shoes parts, climbing-,  cycling and fishing garments and many winter- and summersports textiles. Many of these composites are produced using thermoplastic powders providing specific properties.

Icon
Product Overview Heat Transfer Print | 9.25 MB
Download

Sporttech

Product nameTypeMelting rangeMelt Flow IndexPowder sizesResistance to dry cleaningHand ironEnzyme washingWashing resistanceSteam resistanceStone-wash resistanceHeat resistanceFusing conditions with flow-through-pressAppearance
PastedotDoubledotPowderdotScatterGranulesLamination temperaturePneumatic pressureTime
ROWALIT® 200-2 Copolyamide120 – 130 °C DSC 19 g / 10 Min. (MFI 160°C) 0 – 63 µm
0 – 80 µm		 80 – 200 µm 0 – 160 µm 100 – 500 µm ✓very goodnoyes95 °Cvery goodyes115 °C140 – 160 °C3 – 5 N/cm²12 – 20 Sek.White powder
ROWALIT® 200-7 Copolyamide85 – 95 °C DSC 70 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm ✓ 100 – 500 µm ✓very goodyesno60 °Cmoderateno80 °C95 – 125 °C3 – 5 N/cm²10 – 15 Sek.White powder
ROWALIT® 200-7A Copolyamide85 – 95 °C DSC 90 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm ✓ 100 – 500 µm ✓goodyesno60 °Cmoderateno80 °C95 – 120 °C3 – 5 N/cm²10 – 20 Sek.White powder, Pellets
ROWALIT® 200-8 Copolyamide95 – 105 °C DSC 120 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm ✓ ✓ ✓very goodyes60 °Cmoderate85 °C110 – 140 °C3 – 5 N/cm²10 – 15 Sek.White powder
ROWALIT® 200-11 Copolyamide105 – 115 °C DSC 20 g / 10 Min. (MFI 160°C) 0 – 63 µm
0 – 80 µm		 80 – 200 µm ✓ 100 – 500 µm ✓very goodno60 °Cgood100 °C120 – 140 °C3 – 5 N/cm²10 – 15 Sek.White powder
ROWALIT® 200-14 Biobased Products, Copolyamide110 – 120 °C DSC 30 g / 10 Min. (MFI 160°C) ✓ ✓ ✓ 0 – 500 µm ✓goodno60 °C100 °C120 – 150 °C3 – 5 N/cm²12 – 20 Sek.White powder
ROWALIT® 200-16 Biobased Products, Copolyamide110 – 120 °C DSC 40 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm ✓ ✓ ✓very good60 °C100 °C120 – 140 °C3 – 5 N/cm²10 – 18 Sek.White powder
ROWALIT® 200-20 Copolyamide110 – 120 °C DSC 40 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm 0 – 160 µm ✓ ✓very good60 °Cvery good100 °C125 – 150 °C3 – 5 N/cm²12 – 20 Sek.White powder
ROWALIT® 200-42 Copolyamide105 – 125 °C DSC 40 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm ✓ ✓ ✓very goodno60 °Cmoderateno60 °C130 – 150 °C3 – 5 N/cm²10 – 15 Sek.White powder
ROWALIT® 200-60A Copolyamide110 – 120 °C DSC 90 g / 10 Min. (MFI 160°C) ✕ ✕ ✕ ✕ ✓very good60 °Cgoodno80 °C100 – 140 °C3 – 5 N/cm²12 – 20 Sek.slight transparent granule
ROWALIT® 200-81 Copolyamide105 – 115 °C DSC 70 g / 10 Min. (MFI 160°C) ✕ ✕ ✕ ✕ ✓very good60 °Cgoodno80 °C120 – 140 °C3 – 5 N/cm²12 – 18 Sek.slight transparent granule
ROWALIT® 300-1/18-150 EVA75 – 79 °C DSC 150 g / 10 Min. (MFI 190°C) ✕ ✕ ✕ ✓ ✓40 °C40 °C90 – 95 °C2 – 4 N/cm²3 – 5 Sek.
ROWALIT® 300-1/28-25 EVA65 – 69 °C DSC 25 g / 10 Min. (MFI 190°C) ✕ ✕ ✕ 100 – 400 µm
100 – 500 µm		 ✓40 °C40 °C80 – 85 °C2 – 4 N/cm²3 – 5 Sek.
ROWALIT® 300-1/28-150 EVA65 – 69 °C DSC 150 g / 10 Min. (MFI 190°C) ✕ ✕ ✕ 100 – 400 µm
100 – 500 µm		 ✓40 °C40 °C80 – 85 °C2 – 4 N/cm²3 – 5 Sek.
ROWALIT® 300-1/33-25 EVA59 – 65 °C DSC 25 g / 10 Min. (MFI 190°C) ✕ ✕ ✕ 100 – 500 µm ✓40 °C40 °C75 – 82 °C2 – 4 N/cm²3 – 5 Sek.
ROWALIT® 300-1/33-45 EVA59 – 65 °C DSC 45 g / 10 Min. (MFI 190°C) ✕ ✕ ✕ 100 – 500 µm ✓40 °C40 °C75 – 82 °C2 – 4 N/cm²3 – 5 Sek.
ROWALIT® 300-1/34-25 EVA59 – 65 °C DSC 25 g / 10 Min. (MFI 190°C) ✕ ✕ ✕ 100 – 500 µm ✓40 °C40 °C80 – 100 °C2 – 5 N/cm²3 – 5 Sek.
ROWALIT® 300-1/40-55 EVA55 – 59 °C DSC 55 g / 10 Min. (MFI 190°C) ✕ ✕ ✕ ✓ ✓40 °C40 °C70 – 75 °C2 – 4 N/cm²3 – 5 Sek.
ROWALIT® 400-2 Copolyester110 – 115 °C DSC 15 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm ✕ ✓ ✓goodnono60 °Cfair95 °C130 – 150 °C3 – 10 N/cm²12 – 20 Sek.White powder
ROWALIT® 500-1 TPU90 – 105 °C DSC 4 g / 10 Min. (MFI 160°C) ✕ ✕ ✓ 100 – 500 µm ✓90 °C100 – 120 °C3 – 5 N/cm²10 – 15 Sek.White powder
ROWALIT® 500-3 TPU60 – 80 °C DSC 80 g / 10 Min. (MFI 160°C) ✕ ✕ ✕ 100 – 500 µm ✓fairyes60 °C50 °C75 – 80 °C2 – 4 N/cm²10 – 15 Sek.White powder
ROWALIT® 500-7 TPU62 – 66 °C DSC 20 g / 10 Min. (MFI 160°C) ✕ ✕ ✕ 100 – 500 µm ✓75 – 85 °C2 – 4 N/cm²10 – 15 Sek.
ROWALIT® 500-SIT-23 TPU 20 g / 10 Min. (MFI 160°C) 0 – 63 µm
0 – 80 µm		 80 – 200 µm ✓ 100 – 500 µm ✓goodno60 °Cyes90 °C125 – 145 °C2 – 4 N/cm²12 – 20 Sek.White powder
ROWALIT® 500-SIT-37 TPU115 – 125 °C DSC 20 g / 10 Min. (MFI 160°C) 0 – 63 µm
0 – 80 µm		 80 – 200 µm ✕ 100 – 500 µm ✓good60 °Cyes90 °C120 – 145 °C2 – 4 N/cm²12 – 20 Sek.White powder
ROWALIT® 500-SIT-38 TPU 20 g / 10 Min. (MFI 160°C) 0 – 63 µm
0 – 80 µm		 80 – 200 µm ✕ 100 – 500 µm ✓goodno60 °Cyes90 °C125 – 145 °C2 – 4 N/cm²12 – 20 Sek.White powder
ROWALIT® BIOPOW 5038 Biobased Products, TPU100 – 125 °C DSC 20 g / 10 Min. (MFI 160°C) 0 – 63 µm
0 – 80 µm		 80 – 200 µm ✕ 0 – 500 µm ✓good60 °C90 °C125 – 145 °C2 – 4 N/cm²12 – 20 Sek.White powder
ROWALIT® 500-50 TPU 6 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm ✓ 100 – 500 µm ✓goodyes60 °Cno60 °C120 – 145 °C2 – 4 N/cm²12 – 20 Sek.White powder
ROWALIT® 500-57 TPU 4 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm ✓ 100 – 500 µm ✓goodno60 °Cno90 °C120 – 145 °C2 – 4 N/cm²12 – 20 Sek.White powder
ROWALIT® 500-59 TPU125 – 140 °C DSC 30 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm ✕ 100 – 500 µm ✓goodno90 °Cvery good110 °C140 – 150 °C3 – 5 N/cm²12 – 20 Sek.White powder
ROWALIT® H40 LDPE102 – 106 °C DSC 40 g / 10 Min. (MFI 190°C) ✕ ✕ ✕ ✓ ✓60 °C80 °C130 – 150 °C3 – 5 N/cm²10 – 15 Sek.White powder
ROWALIT® H70 LDPE100 – 104 °C DSC 70 g / 10 Min. (MFI 190°C) ✕ ✕ ✓ ✓ ✓60 °C80 °C130 – 140 °C3 – 5 N/cm²10 – 15 Sek.White powder
ROWALIT® H150 LDPE98 – 102 °C DSC 150 g / 10 Min. (MFI 190°C) ✕ ✕ ✕ ✓ ✓40 °C60 °C120 – 130 °C2 – 5 N/cm²8 – 10 Sek.White powder
ROWAFLEX® TH 4 Thickener ✕ ✕ ✕ ✕ ✕
ROWAFLEX® TH 5 Thickener ✕ ✕ ✕ ✕ ✕
ROWAFLEX® X 800 Dispersions ✕ ✕ ✕ ✕ ✕