Protech characterises textile substrates made of high-performance fiber fabrics providing protection against heat, flames, radiation, liquid metals and ballistic demands. Within this specific marketsegment, protective and functional garments lead to innovations in the fabric market, ie.production of surfaces, finishing, lamination and coating with thermoplastic powders.

Textile packaging materials reflect the purpose of protective and safety textiles for goods (transport) protection. In clean room environments, special garments are needed to prevent contamination, ref. semi-conductor industry or laboratories.

Protech

Product nameTypeMelting rangeMelt Flow IndexPowder sizesResistance to dry cleaningHand ironEnzyme washingWashing resistanceSteam resistanceStone-wash resistanceHeat resistanceFusing conditions with flow-through-pressAppearance
PastedotDoubledotPowderdotScatterGranulesLamination temperaturePneumatic pressureTime
ROWALIT PBT 01-1 PBT220 – 230 °C DSC 115 g / 10 Min. (MFI 230°C) 0 – 80 µm 160 °C250 – 260 °C3 – 5 N/cm²10 – 12 Sek.White powder
BIOPOW® 1038 Biobased Products, Copolyester85 – 85 °C DSC 5 g / 10 Min. (MFI 190°C) 40 °C63 °C125 – 150 °C3 – 5 N/cm²12 – 20 Sek.White powder
ROWALIT 200-13 Copolyamide120 – 130 °C DSC 23 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm 0 – 200 µm 100 – 500 µm very goodnono80 °Cmoderate110 °C130 – 150 °C3 – 5 N/cm²12 – 20 Sek.White powder
ROWALIT 200-27 Copolyamide110 – 120 °C DSC 210 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm very goodno60 °Cvery good150 °C120 – 140 °C3 – 5 N/cm²10 – 15 Sek.White powder
ROWALIT 200-51 Copolyamide125 – 135 °C DSC 25 g / 10 Min. (MFI 160°C) 0 – 80 µm very goodnoyes95 °Cvery goodyes115 °C140 – 160 °C3 – 5 N/cm²10 – 20 Sek.White powder
ROWALIT 200-63 Copolyamide100 – 120 °C DSC 180 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm very good60 °Cgood90 °C110 – 145 °C3 – 5 N/cm²10 – 15 Sek.White powder
ROWALIT 400-2 Copolyester110 – 115 °C DSC 15 g / 10 Min. (MFI 160°C) 0 – 80 µm 80 – 200 µm goodnono60 °Cfair95 °C130 – 150 °C3 – 10 N/cm²12 – 20 Sek.White powder
ROWALIT PET-32 Copolyester140 – 160 °C DSC 5.5 g / 10 Min. (MFI 190°C) 0 – 80 µm 80 – 200 µm 0 – 200 µm 100 – 500 µm no60 °CN/A100 °C140 – 160 °C3 – 5 N/cm²10 – 20 Sek.White powder
ROWALIT 500-SIT-37 TPU115 – 125 °C DSC 20 g / 10 Min. (MFI 160°C) 0 – 63 µm
0 – 80 µm
80 – 200 µm 100 – 500 µm good60 °Cyes90 °C120 – 145 °C2 – 4 N/cm²12 – 20 Sek.White powder
ROWALIT FS-9 Flame-retardant Powders110 – 120 °C DSC 95 °C130 – 160 °C3 – 5 N/cm²10 – 20 Sek.
ROWALIT FS-16 Flame-retardant Powders110 – 120 °C DSC 95 °C
ROWALIT N100-20 HDPE125 – 128 °C DSC 20 g / 10 Min. (MFI 190°C) 0 – 80 µm 80 – 200 µm 0 – 160 µm very goodno95 °Cyes110 °C150 – 170 °C10 – 20 N/cm²10 – 12 Sek.White powder