Buildtech is a synonym for all important and innovations in membrane-, light- and solid construction as well as for earthwork-, water- and road building.

In this segment textiles are applied in ie. concrete armouring, front-building systems, interior work, isolations, waterproof materials, noise prevention or sun protection. Textile substrates in composite materials in roof constructions are bonded with thermoplastic adhesive powders. A combination of high-rigid PES-fabric and laminar coated PTFE can be found in airports, hotels or stadiums.

Product nameTypeMelting rangeMelt Flow IndexPowder sizesResistance to dry cleaningHand ironEnzyme washingWashing resistanceSteam resistanceStone-wash resistanceHeat resistanceFusing conditions with flow-through-pressAppearance
PastedotDoubledotPowderdotScatterGranulesLamination temperaturePneumatic pressureTime
ROWALIT® PBT 01-1 PBT220 – 230 °C DSC 115 g / 10 Min. (MFI 230°C) 0 – 80 µm 160 °C250 – 260 °C3 – 5 N/cm²10 – 12 Sek.White powder
ROWALIT® BIOPOW 4000 Biobased Products, Copolyester100 – 120 °C DSC 1 g / 10 Min. (MFI 190°C) 0 – 80 µm 80 – 200 µm 0 – 200 µm 0 – 300 µm
100 – 500 µm
130 – 150 °C3 – 5 N/cm²12 – 20 Sek.White powder
ROWALIT® 1009 Copolymer Blend65 – 110 °C DSC 90 g / 10 Min. (MFI 190°C) 0 – 400 µm
0 – 500 µm
70 °C120 – 135 °C2 – 5 N/cm²8 – 10 Sek.White powder
ROWALIT® 1014 Copolymer Blend65 – 110 °C DSC 40 g / 10 Min. (MFI 190°C) 0 – 400 µm
0 – 500 µm
75 °C120 – 135 °C2 – 5 N/cm²8 – 10 Sek.White powder
ROWALIT® FS-16 Flame-retardant Powders110 – 120 °C DSC 95 °C
ROWALIT® H8 LDPE107 – 110 °C DSC 8 g / 10 Min. (MFI 190°C) 60 °C80 °C130 – 150 °C3 – 5 N/cm²10 – 15 Sek.White powder
ROWALIT® SS 8 Ionomer95 – 100 °C DSC 6 g / 10 Min. (MFI 190°C) 80 °C130 – 150 °C3 – 5 N/cm²10 – 20 Sek.