The copolyamide series ROWALIT® 200 is mainly applied in the apparel industry as hotmelt adhesive. They cover a melting range of 80-135°C.
Copolyamides are characterized by good adhesion properties on different substrates. Furthermore, they offer good wash- and dry cleaning resistance. Some grades provide steam resistance too.
The above mentioned good properties are upgraded in paste through the usage of plasticizer. This is favourable for further processing and fixation.
Cross-linkable copolyamides are especially interesting for double-dot coating and technical laminates. A duraplastic bonding is achieved through an adjustable cross-linking process.
Product name | Type | Melting range | Melt Flow Index | Powder sizes | Resistance to dry cleaning | Hand iron | Enzyme washing | Washing resistance | Steam resistance | Stone-wash resistance | Heat resistance | Fusing conditions with flow-through-press | Appearance | ||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Pastedot | Doubledot | Powderdot | Scatter | Granules | Lamination temperature | Pneumatic pressure | Time | ||||||||||||
ROWALIT® 200-1 | Copolyamide | 100 – 115 °C DSC | 16 g / 10 Min. (MFI 160°C) |
0 – 63 µm 0 – 80 µm |
80 – 200 µm | ✓ | 100 – 500 µm | ✓ | very good | no | 60 °C | good | 100 °C | 130 – 160 °C | 3 – 5 N/cm² | 10 – 15 Sek. | White Powder | ||
ROWALIT® 200-2 | Copolyamide | 120 – 130 °C DSC | 19 g / 10 Min. (MFI 160°C) |
0 – 63 µm 0 – 80 µm |
80 – 200 µm | 0 – 160 µm | 100 – 500 µm | ✓ | very good | no | yes | 95 °C | very good | yes | 115 °C | 140 – 160 °C | 3 – 5 N/cm² | 12 – 20 Sek. | White powder |
ROWALIT® 200-3 | Biobased Products, Copolyamide | 75 – 85 °C DSC | 90 g / 10 Min. (MFI 160°C) | 0 – 80 µm | 80 – 200 µm | ✓ | ✓ | ✓ | moderate | yes | 40 °C | moderate | 60 °C | 90 – 120 °C | 3 – 5 N/cm² | 10 – 15 Sek. | White powder | ||
ROWALIT® 200-7 | Copolyamide | 85 – 95 °C DSC | 70 g / 10 Min. (MFI 160°C) | 0 – 80 µm | 80 – 200 µm | ✓ | 100 – 500 µm | ✓ | very good | yes | no | 60 °C | moderate | no | 80 °C | 95 – 125 °C | 3 – 5 N/cm² | 10 – 15 Sek. | White powder |
ROWALIT® 200-8 | Copolyamide | 95 – 105 °C DSC | 120 g / 10 Min. (MFI 160°C) | 0 – 80 µm | 80 – 200 µm | ✓ | ✓ | ✓ | very good | yes | 60 °C | moderate | 85 °C | 110 – 140 °C | 3 – 5 N/cm² | 10 – 15 Sek. | White powder | ||
ROWALIT® 200-11 | Copolyamide | 105 – 115 °C DSC | 20 g / 10 Min. (MFI 160°C) |
0 – 63 µm 0 – 80 µm |
80 – 200 µm | ✓ | 100 – 500 µm | ✓ | very good | no | 60 °C | good | 100 °C | 120 – 140 °C | 3 – 5 N/cm² | 10 – 15 Sek. | White powder | ||
ROWALIT® 200-13 | Copolyamide | 120 – 130 °C DSC | 23 g / 10 Min. (MFI 160°C) | 0 – 80 µm | 80 – 200 µm | 0 – 200 µm | 100 – 500 µm | ✕ | very good | no | no | 80 °C | moderate | 110 °C | 130 – 150 °C | 3 – 5 N/cm² | 12 – 20 Sek. | White powder | |
ROWALIT® 200-14 | Biobased Products, Copolyamide | 110 – 120 °C DSC | 30 g / 10 Min. (MFI 160°C) | ✓ | ✓ | ✓ | 0 – 500 µm | ✓ | good | no | 60 °C | 100 °C | 120 – 150 °C | 3 – 5 N/cm² | 12 – 20 Sek. | White powder | |||
ROWALIT® 200-16 | Biobased Products, Copolyamide | 110 – 120 °C DSC | 40 g / 10 Min. (MFI 160°C) | 0 – 80 µm | 80 – 200 µm | ✓ | ✓ | ✓ | very good | 60 °C | 100 °C | 120 – 140 °C | 3 – 5 N/cm² | 10 – 18 Sek. | White powder | ||||
ROWALIT® 200-20 | Copolyamide | 110 – 120 °C DSC | 40 g / 10 Min. (MFI 160°C) | 0 – 80 µm | 80 – 200 µm | 0 – 160 µm | ✓ | ✓ | very good | 60 °C | very good | 100 °C | 125 – 150 °C | 3 – 5 N/cm² | 12 – 20 Sek. | White powder | |||
ROWALIT® 200-27 | Copolyamide | 110 – 120 °C DSC | 210 g / 10 Min. (MFI 160°C) | 0 – 80 µm | 80 – 200 µm | ✕ | ✕ | ✓ | very good | no | 60 °C | very good | 150 °C | 120 – 140 °C | 3 – 5 N/cm² | 10 – 15 Sek. | White powder | ||
ROWALIT® 200-42 | Copolyamide | 105 – 125 °C DSC | 40 g / 10 Min. (MFI 160°C) | 0 – 80 µm | 80 – 200 µm | ✓ | ✓ | ✓ | very good | no | 60 °C | moderate | no | 60 °C | 130 – 150 °C | 3 – 5 N/cm² | 10 – 15 Sek. | White powder | |
ROWALIT® 200-51 | Copolyamide | 125 – 135 °C DSC | 25 g / 10 Min. (MFI 160°C) | 0 – 80 µm | ✓ | ✕ | ✕ | ✓ | very good | no | yes | 95 °C | very good | yes | 115 °C | 140 – 160 °C | 3 – 5 N/cm² | 10 – 20 Sek. | White powder |
ROWALIT® 200-60A | Copolyamide | 110 – 120 °C DSC | 90 g / 10 Min. (MFI 160°C) | ✕ | ✕ | ✕ | ✕ | ✓ | very good | 60 °C | good | no | 80 °C | 100 – 140 °C | 3 – 5 N/cm² | 12 – 20 Sek. | slight transparent granule | ||
ROWALIT® 200-63 | Copolyamide | 100 – 120 °C DSC | 180 g / 10 Min. (MFI 160°C) | 0 – 80 µm | 80 – 200 µm | ✕ | ✓ | ✓ | very good | 60 °C | good | 90 °C | 110 – 145 °C | 3 – 5 N/cm² | 10 – 15 Sek. | White powder |