Use the filter functions to specifically select products by properties, application areas, certifications, or technical parameters. Then click ‘Filter…’ to update the product overview according to your selection.

Product Name Download Type Melting range Melt Flow Index Powder Sizes
Pastedot Doubledot Powderdot Scatter Granules
Ratio of renewable raw materials Eco-Passport Biodegradability Resistance to dry cleaning Washing resistance Heat resistance Fusing conditions with flow-through-press Appearance
BIOPOW® 1038 Bio-based products, Copolyester 85 – 85 °C DSC 5 g / 10 Min. (MFI 190°C)
✓
35 % yes (Home & Soil) 40 °C 63 °C Lamination temperature: 125 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
BIOPOW® 1036 Bio-based products, Copolyester 115 – 115 °C DSC 22 g / 10 Min. (MFI 190°C)
0 – 80 µm 80 – 200 µm 100 – 500 µm ✓
51 % ✓ yes (industrial) 60 °C 95 °C Lamination temperature: 125 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
BIOPOW® 1043 Bio-based products, Copolyester 115 – 115 °C DSC 22 g / 10 Min. (MFI 190°C)
0 – 80 µm 80 – 200 µm 100 – 500 µm ✓
100 % yes (industrial) 60 °C 95 °C Lamination temperature: 125 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
BIOPOW® 4000 Bio-based products, Copolyester 110 – 120 °C DSC 1 g / 10 Min. (MFI 190°C)
0 – 80 µm 80 – 200 µm 0 – 200 µm 0 – 300 µm
100 – 500 µm		 ✓
40 % ✓ yes (Home & Soil) Lamination temperature: 130 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
BIOPOW® 4042 Bio-based products, Copolyester 65 – 75 °C DSC 55 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm ✓
60 % yes (industrial) moderate 40 °C 55 °C Lamination temperature: 80 – 110 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
BIOPOW® 4045 Bio-based products, Copolyester 110 – 120 °C DSC 25 g / 10 Min. (MFI 190°C)
0 – 80 µm 80 – 200 µm 100 – 500 µm ✓
95 % ✓ yes (home, industrial) 60 °C 95 °C Lamination temperature: 125 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
BIOPOW® 4046 Bio-based products, Copolyester 110 – 120 °C DSC 4.5 g / 10 Min. (MFI 190°C)
0 – 80 µm 80 – 200 µm 100 – 500 µm ✓
99 % yes (industrial, Home in test period) Lamination temperature: 125 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
BIOPOW® 5038 Bio-based products, TPU 100 – 125 °C DSC 20 g / 10 Min. (MFI 160°C)
0 – 63 µm
0 – 80 µm		 80 – 200 µm 0 – 500 µm ✓
40 % no good 60 °C 90 °C Lamination temperature: 125 – 145 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 12 – 20 seconds 		White powder
ROWAFLEX™ DF 2 Defoamer
✓ slight yellowish opaque
ROWAFLEX™ TH 3 Thickener
✓ Slight yellowish, low-viscous liquid dispersion
ROWAFLEX™ TH 4 Thickener
0 % ✓ yes (89%) Slight yellowish, low-viscous liquid dispersion
ROWAFLEX™ TH 5 Thickener
0 % yes (89%) Slight yellowish, low-viscous liquid dispersion
ROWAFLEX™ X 100 Paste Stabilizer
opaque, ropy liquid
ROWAFLEX™ X 502 Plasticizer
✓ Colorless liquid
ROWAFLEX™ X 572 Emulsifier
✓ Clear to cloudy liquid
ROWAFLEX™ X 600 Crosslinker
clear, almost colorless liquid
ROWAFLEX™ X 800 Dispersions / Solutions
Opaque white liquid
ROWALIT™ 1009 Copolymer Blend 65 – 110 °C DSC 90 g / 10 Min. (MFI 190°C)
0 – 400 µm
0 – 500 µm
0 % no 70 °C Lamination temperature: 120 – 135 °C
Pneumatic pressure: 2 – 5 N/cm²
Time: 8 – 10 seconds 		White powder
ROWALIT™ 1014 Copolymer Blend 65 – 110 °C DSC 40 g / 10 Min. (MFI 190°C)
0 – 400 µm
0 – 500 µm
0 % no 75 °C Lamination temperature: 120 – 135 °C
Pneumatic pressure: 2 – 5 N/cm²
Time: 8 – 10 seconds 		White powder
ROWALIT™ 200-1 Copolyamide 100 – 115 °C DSC 16 g / 10 Min. (MFI 160°C)
0 – 63 µm
0 – 80 µm		 80 – 200 µm ✓ 100 – 500 µm ✓
✓ no very good 60 °C 100 °C Lamination temperature: 130 – 160 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds 		White Powder
ROWALIT™ 200-11 Copolyamide 105 – 115 °C DSC 20 g / 10 Min. (MFI 160°C)
0 – 63 µm
0 – 80 µm		 80 – 200 µm 100 – 500 µm ✓
✓ no very good 60 °C 100 °C Lamination temperature: 120 – 140 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ 200-13 Copolyamide 120 – 130 °C DSC 23 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm 0 – 200 µm 100 – 500 µm
no very good 80 °C 110 °C Lamination temperature: 130 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
ROWALIT™ 200-14 Bio-based products, Copolyamide 110 – 120 °C DSC 30 g / 10 Min. (MFI 160°C)
0 – 500 µm ✓
38 % ✓ no good 60 °C 100 °C Lamination temperature: 120 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
ROWALIT™ 200-16 Bio-based products, Copolyamide 110 – 120 °C DSC 40 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm ✓ ✓
42 % no very good 60 °C Lamination temperature: 120 – 140 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 18 seconds 		White powder
ROWALIT™ 200-2 Copolyamide 120 – 130 °C DSC 19 g / 10 Min. (MFI 160°C)
0 – 63 µm
0 – 80 µm		 80 – 200 µm 0 – 160 µm 100 – 500 µm ✓
0 % ✓ no very good 95 °C 115 °C Lamination temperature: 140 – 160 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
ROWALIT™ 200-20 Copolyamide 110 – 120 °C DSC 40 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm 0 – 160 µm ✓ ✓
0 % no very good 60 °C 100 °C Lamination temperature: 125 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
ROWALIT™ 200-27 Copolyamide 110 – 120 °C DSC 210 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm ✓
0 % ✓ no very good 60 °C 150 °C Lamination temperature: 120 – 140 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ 200-3 Bio-based products, Copolyamide 75 – 85 °C DSC 90 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm ✓
90 % no very good 40 °C 60 °C Lamination temperature: 90 – 120 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ 200-42 Copolyamide 105 – 125 °C DSC 40 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm ✓
0 % no very good 60 °C 60 °C Lamination temperature: 130 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ 200-51 Copolyamide 125 – 135 °C DSC 25 g / 10 Min. (MFI 160°C)
0 – 80 µm ✓ ✓
✓ no very good 95 °C 115 °C Lamination temperature: 140 – 160 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 20 seconds 		White powder
ROWALIT™ 200-60A Copolyamide 110 – 120 °C DSC 90 g / 10 Min. (MFI 160°C)
✓
0 % no very good 60 °C 80 °C Lamination temperature: 100 – 140 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		slight transparent granule
ROWALIT™ 200-63 Copolyamide 100 – 120 °C DSC 180 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm ✓
0 % ✓ no very good 60 °C 90 °C Lamination temperature: 110 – 145 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ 200-7 Copolyamide 85 – 95 °C DSC 70 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm 100 – 500 µm ✓
20 % no very good 60 °C 80 °C Lamination temperature: 95 – 125 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ 200-7A Copolyamide 85 – 95 °C DSC 90 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm 100 – 500 µm ✓
90 % no good 50 °C 80 °C Lamination temperature: 95 – 120 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 20 seconds 		White powder, Pellets
ROWALIT™ 200-8 Copolyamide 95 – 105 °C DSC 120 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm ✓
0 % no very good 60 °C 85 °C Lamination temperature: 110 – 140 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ 200-81 Copolyamide 105 – 115 °C DSC 70 g / 10 Min. (MFI 160°C)
✓
40 % no very good 60 °C 80 °C Lamination temperature: 120 – 140 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 18 seconds 		slight transparent granule
ROWALIT™ 200-86 Copolyamide 105 – 115 °C DSC 6 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm 0 – 160 µm 100 – 500 µm ✓
nein very good 60 °C 100 °C Lamination temperature: 120 – 140 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
ROWALIT™ 300-1/18-150 EVA 75 – 79 °C DSC 150 g / 10 Min. (MFI 190°C)
✓
40 °C 40 °C Lamination temperature: 90 – 95 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 3 – 5 seconds 		White powder
ROWALIT™ 300-1/28-150 EVA 65 – 69 °C DSC 150 g / 10 Min. (MFI 190°C)
100 – 400 µm
100 – 500 µm		 ✓
✓ 40 °C 40 °C Lamination temperature: 80 – 85 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 3 – 5 seconds 		White powder
ROWALIT™ 300-1/28-20 EVA 65 – 69 °C DSC 20 g / 10 Min. (MFI 190°C)
100 – 400 µm
100 – 500 µm		 ✓
✓ 40 °C 50 °C Lamination temperature: 80 – 85 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 3 – 5 seconds 		White powder
ROWALIT™ 300-1/28-25 EVA 65 – 69 °C DSC 25 g / 10 Min. (MFI 190°C)
100 – 400 µm
100 – 500 µm		 ✓
✓ 40 °C 40 °C Lamination temperature: 80 – 85 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 3 – 5 seconds 		White powder
ROWALIT™ 300-1/33-25 EVA 59 – 65 °C DSC 25 g / 10 Min. (MFI 190°C)
100 – 500 µm ✓
✓ 40 °C 40 °C Lamination temperature: 75 – 82 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 3 – 5 seconds 		White powder
ROWALIT™ 300-1/33-45 EVA 59 – 65 °C DSC 45 g / 10 Min. (MFI 190°C)
100 – 500 µm ✓
40 °C 40 °C Lamination temperature: 75 – 82 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 3 – 5 seconds 		White powder
ROWALIT™ 300-1/34-25 EVA 59 – 65 °C DSC 25 g / 10 Min. (MFI 190°C)
100 – 500 µm ✓
✓ 40 °C 40 °C Lamination temperature: 80 – 100 °C
Pneumatic pressure: 2 – 5 N/cm²
Time: 3 – 5 seconds 		White powder
ROWALIT™ 300-1/40-55 EVA 55 – 59 °C DSC 55 g / 10 Min. (MFI 190°C)
✓
✓ 40 °C 40 °C Lamination temperature: 70 – 75 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 3 – 5 seconds 		White powder
ROWALIT™ 400-1 Copolyester 118 – 123 °C DSC 30 g / 10 Min. (MFI 160°C)
0 – 63 µm
0 – 80 µm		 80 – 160 µm
80 – 200 µm		 0 – 160 µm 100 – 500 µm ✓
0 % no good 80 °C 100 °C Lamination temperature: 130 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 12 seconds 		White powder
ROWALIT™ 400-14 Copolyester 177 – 186 °C DSC 110 g / 10 Min. (MFI 190°C)
0 – 80 µm ✓
40 % no good 90 °C 140 °C Lamination temperature: 210 – 230 °C
Pneumatic pressure: 3 – 10 N/cm²
Time: 12 – 20 seconds 		White powder
ROWALIT™ 400-2 Copolyester 110 – 115 °C DSC 15 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm ✓
0 % no good 60 °C 95 °C Lamination temperature: 130 – 150 °C
Pneumatic pressure: 3 – 10 N/cm²
Time: 12 – 20 seconds 		White powder
ROWALIT™ 400-20 Copolyester 70 – 85 °C DSC 150 g / 10 Min. (MFI 160°C)
✓
0 % no low 40 °C 70 °C Lamination temperature: 90 – 120 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ 400-21 Bio-based products, Copolyester 60 – 75 °C DSC 35 g / 10 Min. (MFI 190°C)
0 – 80 µm 80 – 160 µm
80 – 200 µm		 0 – 200 µm 100 – 500 µm ✓
0 % yes (Home & Soil / Industrial / Marine) 30 °C Lamination temperature: 75 – 95 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 25 seconds 		White powder
ROWALIT™ 400-29 Bio-based products, Copolyester 110 – 120 °C DSC 34 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm ✓
30 % ✓ no good 60 °C 100 °C Lamination temperature: 120 – 140 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 12 seconds 		White Powder
ROWALIT™ 400-32 Copolyester 140 – 160 °C DSC 5.5 g / 10 Min. (MFI 190°C)
0 – 80 µm 80 – 200 µm 0 – 200 µm 100 – 500 µm ✓
0 % 60 °C 130 °C Lamination temperature: 160 – 190 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 20 seconds 		White powder
ROWALIT™ 400-37M Copolyester 110 – 120 °C DSC 20 g / 10 Min. (MFI 160°C)
0 – 63 µm
0 – 80 µm		 80 – 200 µm ✓
0 % ✓ no good 60 °C 100 °C Lamination temperature: 115 – 140 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 20 seconds 		White powder
ROWALIT™ 400-40 Copolyester 105 – 120 °C DSC 40 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm ✓ ✓
0 % ✓ no good 60 °C 100 °C Lamination temperature: 115 – 130 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 20 seconds 		White powder
ROWALIT™ 400-41 Bio-based products, Copolyester 110 – 120 °C DSC 20 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm ✓
0 % yes (Home & Soil) moderate 40 °C 100 °C Lamination temperature: 125 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
ROWALIT™ 400-44 Bio-based products, Copolyester 110 – 120 °C DSC 45 g / 10 Min. (MFI 160°C)
0 – 63 µm
0 – 80 µm		 80 – 200 µm 100 – 500 µm ✓
30 % no good 60 °C 100 °C Lamination temperature: 115 – 130 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 20 seconds 		White powder
ROWALIT™ 400-8 Copolyester 118 – 125 °C DSC 35 g / 10 Min. (MFI 160°C)
0 – 80 µm
0 % ✓ no fair 60 °C 100 °C Lamination temperature: 125 – 145 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
ROWALIT™ 400-SIT-18 Copolyester 110 – 120 °C DSC 30 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm ✓
30 % good 60 °C 80 °C Lamination temperature: 110 – 135 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 20 seconds 		White powder
ROWALIT™ 500-1 TPU 90 – 105 °C DSC 4 g / 10 Min. (MFI 160°C)
100 – 500 µm ✓
no 90 °C Lamination temperature: 100 – 120 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ 500-3 TPU 60 – 80 °C DSC 80 g / 10 Min. (MFI 160°C)
100 – 500 µm ✓
no fair 60 °C 50 °C Lamination temperature: 75 – 80 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ 500-50 TPU 6 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm 100 – 500 µm ✓
0 % ✓ no good 60 °C 60 °C Lamination temperature: 120 – 145 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 10 – 20 seconds 		White powder
ROWALIT™ 500-57 TPU 4 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm 100 – 500 µm ✓
0 % ✓ no good 60 °C 90 °C Lamination temperature: 120 – 145 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 10 – 20 seconds 		White powder
ROWALIT™ 500-59 TPU 125 – 140 °C DSC 30 g / 10 Min. (MFI 160°C)
0 – 80 µm 80 – 200 µm 100 – 500 µm ✓
✓ no good 90 °C 110 °C Lamination temperature: 140 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 12 – 20 seconds 		White powder
ROWALIT™ 500-7 TPU 62 – 66 °C DSC 20 g / 10 Min. (MFI 160°C)
100 – 500 µm ✓
fair Lamination temperature: 75 – 85 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ 500-SIT-23 TPU 20 g / 10 Min. (MFI 160°C)
0 – 63 µm
0 – 80 µm		 80 – 200 µm 100 – 500 µm ✓
✓ no good 60 °C 90 °C Lamination temperature: 125 – 145 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 12 – 20 seconds 		White powder
ROWALIT™ 500-SIT-37 TPU 115 – 125 °C DSC 20 g / 10 Min. (MFI 160°C)
0 – 63 µm
0 – 80 µm		 80 – 200 µm 100 – 500 µm ✓
0 % ✓ no good 60 °C 90 °C Lamination temperature: 120 – 145 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 12 – 20 seconds 		White powder
ROWALIT™ 500-SIT-38 TPU 20 g / 10 Min. (MFI 160°C)
0 – 63 µm
0 – 80 µm		 80 – 200 µm 100 – 500 µm ✓
0 % ✓ no good 60 °C 90 °C Lamination temperature: 125 – 145 °C
Pneumatic pressure: 2 – 4 N/cm²
Time: 12 – 20 seconds 		White powder
ROWALIT™ 600-1 Polypropylene 132 – 136 °C DSC 4 g / 10 Min. (MFI 190°C) 8 g / 10 Min. (MFI 230°C)
80 – 200 µm 0 – 200 µm
✓ 95 °C 115 °C Lamination temperature: 140 – 180 °C
Pneumatic pressure: 3 – 6 N/cm²
Time: 12 – 30 seconds 		Powder
ROWALIT™ 690 Polypropylene 150 – 165 °C DSC 20 g / 10 Min. (MFI 190°C)
✓
95 °C 150 °C Lamination temperature: 160 – 200 °C
Pneumatic pressure: 3 – 6 N/cm²
Time: 12 – 25 seconds 		Pellets, Powder
ROWALIT™ FS-16 Flame Retardancy 110 – 120 °C DSC
95 °C White, weak odouros Powder
ROWALIT™ FS-9 Flame Retardancy 110 – 120 °C DSC
95 °C Lamination temperature: 130 – 160 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 20 seconds 		White powder
ROWALIT™ H150 LDPE 98 – 102 °C DSC 150 g / 10 Min. (MFI 190°C)
✓
0 % no 40 °C 60 °C Lamination temperature: 120 – 130 °C
Pneumatic pressure: 2 – 5 N/cm²
Time: 8 – 10 seconds 		White powder
ROWALIT™ H20 LDPE 104 – 108 °C DSC 20 g / 10 Min. (MFI 190°C)
✓
0 % nein 60 °C 80 °C Lamination temperature: 130 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ H40 LDPE 102 – 106 °C DSC 40 g / 10 Min. (MFI 190°C)
✓
0 % ✓ 60 °C 80 °C Lamination temperature: 130 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ H70 LDPE 100 – 104 °C DSC 70 g / 10 Min. (MFI 190°C)
✓
0 % ✓ no 60 °C 80 °C Lamination temperature: 130 – 140 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ H8 LDPE 107 – 110 °C DSC 8 g / 10 Min. (MFI 190°C)
✓
0 % ✓ nein 60 °C 80 °C Lamination temperature: 130 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds 		White powder
ROWALIT™ N100-20 HDPE 125 – 128 °C DSC 20 g / 10 Min. (MFI 190°C)
0 – 80 µm 80 – 200 µm 0 – 160 µm
✓ sehr gut 95 °C 110 °C Lamination temperature: 150 – 170||170 °C
Pneumatic pressure: 10||10 – 20 N/cm²
Time: 10 – 12 seconds 		Weisses Pulver
ROWALIT™ N100-3 HDPE 130 – 135 °C DSC 4 g / 10 Min. (MFI 190°C)
0 – 80 µm
no very good 95 °C 110 °C Lamination temperature: 170 – 180||180 °C
Pneumatic pressure: 15||15 – 25||25 N/cm²
Time: 12 – 18 seconds 		White powder
ROWALIT™ N100-6 HDPE 128 – 130 °C DSC 6 g / 10 Min. (MFI 190°C)
0 – 80 µm 80 – 200 µm
✓ no very good 95 °C 110 °C Lamination temperature: 155 – 170 °C
Pneumatic pressure: 10 – 20 N/cm²
Time: 12 – 18 seconds 		White powder
ROWALIT™ PBT 01-1 PBT 220 – 230 °C DSC 115 g / 10 Min. (MFI 230°C)
0 – 80 µm
160 °C Lamination temperature: 250 – 260 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 12 seconds 		White powder
ROWALIT™ PET-32 Copolyester 140 – 160 °C DSC 5.5 g / 10 Min. (MFI 190°C)
0 – 80 µm 80 – 200 µm 0 – 200 µm 100 – 500 µm ✓
0 % no 60 °C 100 °C Lamination temperature: 160 – 190 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 20 seconds 		White powder
ROWALIT™ SS 8 Ionomer 95 – 100 °C DSC 6 g / 10 Min. (MFI 190°C)
80 °C Lamination temperature: 130 – 150 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 20 seconds 		White powder
ROWAK

ROWAK AG Switzerland
Headquarters
Hadlaubstrasse 66
8006 Zürich

+41 (0)43 300 53 33
info@rowak.ch

ROWAK AG Germany
Chemical factory
Schmittenstrasse 21
79771 Klettgau-Griessen

+49 (0)7742 15 25
info@rowak.de

Products & Solutions
Service & Support
Innovation R&D
Markets
Company
Contact

Customer Service
Sustainability
Job Vacancies
Certificates
Legal
ROWALIT™ 500-SIT-23
ROWALIT™ 500-59
ROWALIT™ H70
ROWALIT™ 300-1/28-150
BIOPOW® 4000
Our History
Why an octopus?

Productfinder

© 2026 ROWAK AG

Legal Notice

Privacy Policy

Terms and Conditions

brand & design by ef+es / coding by deutz produktionsstudios

Legal Notice

Privacy Policy

Terms and Conditions

© 2026 ROWAK AG

brand & design by ef+es
coding by deutz produktionsstudios

Legal Notice
Privacy Policy
Terms and Conditions

Rowak