ROWALIT N100-3
High-Density-Polyethylene Powder
High-Density-Polyethylene Powder
Type
HDPE
Chemical character
High-Density-Polyethylene
Melting range
130 – 135 °C DSC
Vicat softening point
123 – 128 °C (ISO 306)
Melt Flow Index
4 g / 10 Min. (MFI 190°C / 2,16 kg)
Density
944 kg/m³
Powder sizes
Pastedot (0 – 80 µm)
Doubledot
Powderdot
Scatter
Other sizes upon request
Doubledot
Powderdot
Scatter
Other sizes upon request
Ratio of renewable raw materials
0 %
Biodegradability
no
Washing resistance
95 °C
Dry cleaning resistance
very good
Heat resistance
110 °C
Hand iron
no
Steam resistance
yes
Appearance
White powder
Fusing conditions with flow-through-press
Lamination temperature: 170 – 180 °C
Pneumatic pressure: 15 – 25 N/cm²
Time: 12 – 18 seconds
Pneumatic pressure: 15 – 25 N/cm²
Time: 12 – 18 seconds