ROWALIT 200-63
Copolyamide
Copolyamide
Type
Copolyamide
Chemical character
Copolyamide
Melting range
100 – 120 °C DSC
Melt Flow Index
180 g / 10 Min. (MFI 160°C / 2,16 kg)
Powder sizes
Pastedot (0 – 80 µm)
Doubledot (80 – 200 µm)
Scatter
Granules
Doubledot (80 – 200 µm)
Scatter
Granules
Ratio of renewable raw materials
0 %
Biodegradability
no
Washing resistance
60 °C
Dry cleaning resistance
very good
Heat resistance
90 °C
Steam resistance
good
Appearance
White powder
Fusing conditions with flow-through-press
Lamination temperature: 110 – 145 °C
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds
Pneumatic pressure: 3 – 5 N/cm²
Time: 10 – 15 seconds
Application
Interlinings with fusing conditions and low viscosity at good fastness profile; siliconized fabrics; in paste dot coating as crosslinkable thermoplast as base dot in doubledot process or single dot in direct lamination – outstanding fastnesses are reached
Recipe recommendation
Crosslinkable Paste
Water / H2O | 55 kg |
ROWAFLEX DF 2 | 0.2 kg |
ROWAFLEX X 600 | 3 kg |
ROWALIT 200-63, 0-80 | 30 kg |
ROWAFLEX TH 3 | 0.4 kg |
ROWAFLEX X 100 | 10 kg |