Copolyester

The copolyester series ROWALIT™ 400 is applied in the apparel industry and steadily expanding in technical items. They cover a melting range of 80-135°C.

Copolyester hotmelt adhesives offer good bond strength and wash resistance on PES and traditional blends like PES/Cotton textiles. Dry cleaning resistance is limited.

Product Name

Download

Type

Melting range

Melt Flow Index

Powder Sizes

Pastedot

Doubledot

Powderdot

Scatter

Granules

Ratio of renewable raw materials

Eco-Passport

Biodegradability

Resistance to dry cleaning

Washing resistance

Heat resistance

Fusing conditions with flow-through-press

Appearance

ROWALIT™ 400-1

Copolyester

118 – 123 °C DSC

30 g / 10 Min. (MFI 160°C)

0 – 63 µm
0 – 80 µm

80 – 160 µm
80 – 200 µm

0 – 160 µm

100 – 500 µm

✓

0 %

good

80 °C

100 °C

Fugentemperatur: 130 – 150 °C
Druck: 3 – 5 N/cm²
Zeit: 10 – 12 Sekunden

White powder

ROWALIT™ 400-14

Copolyester

177 – 186 °C DSC

110 g / 10 Min. (MFI 190°C)

0 – 80 µm

✓

40 %

good

90 °C

140 °C

Fugentemperatur: 210 – 230 °C
Druck: 3 – 10 N/cm²
Zeit: 12 – 20 Sekunden

White powder

ROWALIT™ 400-2

Copolyester

110 – 115 °C DSC

15 g / 10 Min. (MFI 160°C)

0 – 80 µm

80 – 200 µm

✓

0 %

good

60 °C

95 °C

Fugentemperatur: 130 – 150 °C
Druck: 3 – 10 N/cm²
Zeit: 12 – 20 Sekunden

White powder

ROWALIT™ 400-20

Copolyester

70 – 85 °C DSC

150 g / 10 Min. (MFI 160°C)

✓

0 %

low

40 °C

70 °C

Fugentemperatur: 90 – 120 °C
Druck: 2 – 4 N/cm²
Zeit: 10 – 15 Sekunden

White powder

ROWALIT™ 400-21

Bio-based products, Copolyester

60 – 75 °C DSC

35 g / 10 Min. (MFI 190°C)

0 – 80 µm

80 – 160 µm
80 – 200 µm

0 – 200 µm

100 – 500 µm

✓

0 %

yes (Home & Soil / Industrial / Marine)

30 °C

Fugentemperatur: 75 – 95 °C
Druck: 3 – 5 N/cm²
Zeit: 10 – 25 Sekunden

White powder

ROWALIT™ 400-29

Bio-based products, Copolyester

110 – 120 °C DSC

34 g / 10 Min. (MFI 160°C)

0 – 80 µm

80 – 200 µm

✓

30 %

✓

good

60 °C

100 °C

Fugentemperatur: 120 – 140 °C
Druck: 3 – 5 N/cm²
Zeit: 10 – 12 Sekunden

White Powder

ROWALIT™ 400-32

Copolyester

140 – 160 °C DSC

5.5 g / 10 Min. (MFI 190°C)

0 – 80 µm

80 – 200 µm

0 – 200 µm

100 – 500 µm

✓

0 %

60 °C

130 °C

Fugentemperatur: 160 – 190 °C
Druck: 3 – 5 N/cm²
Zeit: 10 – 20 Sekunden

White powder

ROWALIT™ 400-37M

Copolyester

110 – 120 °C DSC

20 g / 10 Min. (MFI 160°C)

0 – 63 µm
0 – 80 µm

80 – 200 µm

✓

0 %

✓

good

60 °C

100 °C

Fugentemperatur: 115 – 140 °C
Druck: 3 – 5 N/cm²
Zeit: 10 – 20 Sekunden

White powder

ROWALIT™ 400-40

Copolyester

105 – 120 °C DSC

40 g / 10 Min. (MFI 160°C)

0 – 80 µm

80 – 200 µm

✓

0 %

✓

good

60 °C

100 °C

Fugentemperatur: 115 – 130 °C
Druck: 3 – 5 N/cm²
Zeit: 10 – 20 Sekunden

White powder

ROWALIT™ 400-41

Bio-based products, Copolyester

110 – 120 °C DSC

20 g / 10 Min. (MFI 160°C)

0 – 80 µm

80 – 200 µm

✓

0 %

yes (Home & Soil)

moderate

40 °C

100 °C

Fugentemperatur: 125 – 150 °C
Druck: 3 – 5 N/cm²
Zeit: 12 – 20 Sekunden

White powder

ROWALIT™ 400-44

Bio-based products, Copolyester

110 – 120 °C DSC

45 g / 10 Min. (MFI 160°C)

0 – 63 µm
0 – 80 µm

80 – 200 µm

100 – 500 µm

✓

30 %

good

60 °C

100 °C

Fugentemperatur: 115 – 130 °C
Druck: 3 – 5 N/cm²
Zeit: 10 – 20 Sekunden

White powder

ROWALIT™ 400-8

Copolyester

118 – 125 °C DSC

35 g / 10 Min. (MFI 160°C)

0 – 80 µm

0 %

✓

fair

60 °C

100 °C

Fugentemperatur: 125 – 145 °C
Druck: 3 – 5 N/cm²
Zeit: 12 – 20 Sekunden

White powder

ROWALIT™ 400-SIT-18

Copolyester

110 – 120 °C DSC

30 g / 10 Min. (MFI 160°C)

0 – 80 µm

80 – 200 µm

✓

30 %

good

60 °C

80 °C

Fugentemperatur: 110 – 135 °C
Druck: 3 – 5 N/cm²
Zeit: 10 – 20 Sekunden

White powder

ROWALIT™ PET-32

Copolyester

140 – 160 °C DSC

5.5 g / 10 Min. (MFI 190°C)

0 – 80 µm

80 – 200 µm

0 – 200 µm

100 – 500 µm

✓

0 %

60 °C

100 °C

Fugentemperatur: 160 – 190 °C
Druck: 3 – 5 N/cm²
Zeit: 10 – 20 Sekunden

White powder