Sporttech
Textiles with broad functionality are increasingly popular within the sports- and leisure industry. Athletes wear sports cloths with thermal regulative properties. That has commonly applied in many high-quality outdoor products.
Further sports-oriented textile areas are various shoes parts, climbing-, cycling and fishing garments and many winter- and summersports textiles. Many of these composites are produced using thermoplastic powders providing specific properties.


Type | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide |
Melting range / °C DSC | 120 - 130 | 110 - 120 | 85 - 95 | 95 - 105 | 105 - 115 | 110 - 120 | 105 - 125 | 110 - 120 |
Melting viscosity / g | ||||||||
MFI 160°C, 2.16 kg, 10 min. | 19 | 50 | 70 | 120 | 20 | 40 | 40 | 90 |
Chemical Basis | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide |
Powder sizes | ||||||||
Pastedot | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Doubledot | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Powderdot | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Scatter | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Granules | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Resistance to dry cleaning | very good | very good | very good | very good | very good | very good | very good | very good |
Washing resistance in °C |
95°C | 40°C | 60°C | 60°C | 60°C | 60°C | 60°C | 60°C |
Fusing conditions with flow-through-press | ||||||||
Lamination temperature in °C | 140 - 160 | 115 - 135 | 95 - 125 | 110 - 140 | 120 - 140 | 125 - 150 | 130 - 150 | 100 - 140 |
Pneumatic pressure N / cm² | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 |
Time in sec. | 12 - 20 | 10 - 15 | 10 - 15 | 10 - 15 | 10 - 15 | 12 - 20 | 10 - 15 | 12 - 20 |
Appearance | White powder | White Powder | White powder | White powder | White powder | White powder | White powder | slight transparent granule |
Type | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide |
Melting range / °C DSC | 120 - 130 | 110 - 120 | 85 - 95 | 95 - 105 | 105 - 115 | 110 - 120 | 105 - 125 | 110 - 120 |
Melting viscosity / g | ||||||||
MFI 160°C, 2.16 kg, 10 min. | 19 | 50 | 70 | 120 | 20 | 40 | 40 | 90 |
Chemical Basis | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide | Copolyamide |
Powder sizes | ||||||||
Pastedot | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Doubledot | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Powderdot | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Scatter | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Granules | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Resistance to dry cleaning | very good | very good | very good | very good | very good | very good | very good | very good |
Washing resistance in °C |
95°C | 40°C | 60°C | 60°C | 60°C | 60°C | 60°C | 60°C |
Fusing conditions with flow-through-press | ||||||||
Lamination temperature in °C | 140 - 160 | 115 - 135 | 95 - 125 | 110 - 140 | 120 - 140 | 125 - 150 | 130 - 150 | 100 - 140 |
Pneumatic pressure N / cm² | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 |
Time in sec. | 12 - 20 | 10 - 15 | 10 - 15 | 10 - 15 | 10 - 15 | 12 - 20 | 10 - 15 | 12 - 20 |
Appearance | White powder | White Powder | White powder | White powder | White powder | White powder | White powder | slight transparent granule |
Type | EVA | EVA | EVA | EVA | EVA |
Melting range / °C DSC | 75 - 79 | 65 - 69 | 59 - 65 | 59 - 65 | 55 - 59 |
Melting viscosity / g | |||||
MFI 190°C, 2.16 kg, 10 min. | 150 | 150 | 25 | 45 | 55 |
Chemical Basis | Ethylene-Vinyl-Acetate | Ethylene-Vinyl-Acetate | Ethylene-Vinyl-Acetate | Ethylene-Vinyl-Acetate | Ethylene-Vinyl-Acetate |
VA-Content (%) | 18% | 28% | 33% | 33% | 40% |
Powder sizes | |||||
Pastedot | ![]() | ![]() | ![]() | ![]() | ![]() |
Doubledot | ![]() | ![]() | ![]() | ![]() | ![]() |
Powderdot | ![]() | ![]() | ![]() | ![]() | ![]() |
Scatter | ![]() | ![]() | ![]() | ![]() | ![]() |
Granules | ![]() | ![]() | ![]() | ![]() | ![]() |
Washing resistance in °C |
40°C | 40°C | 40°C | 40°C | 40°C |
Fusing conditions with flow-through-press | |||||
Lamination temperature in °C | 90 - 95 | 80 - 85 | 75 - 82 | 75 - 82 | 70 - 75 |
Pneumatic pressure N / cm² | 2 - 4 | 2 - 4 | 2 - 4 | 2 - 4 | 2 - 4 |
Time in sec. | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 |
Appearance | White powder | White powder | White powder | White powder | White powder |
Type | EVA | EVA | EVA | EVA | EVA |
Melting range / °C DSC | 75 - 79 | 65 - 69 | 59 - 65 | 59 - 65 | 55 - 59 |
Melting viscosity / g | |||||
MFI 190°C, 2.16 kg, 10 min. | 150 | 150 | 25 | 45 | 55 |
Chemical Basis | Ethylene-Vinyl-Acetate | Ethylene-Vinyl-Acetate | Ethylene-Vinyl-Acetate | Ethylene-Vinyl-Acetate | Ethylene-Vinyl-Acetate |
VA-Content (%) | 18% | 28% | 33% | 33% | 40% |
Powder sizes | |||||
Pastedot | ![]() | ![]() | ![]() | ![]() | ![]() |
Doubledot | ![]() | ![]() | ![]() | ![]() | ![]() |
Powderdot | ![]() | ![]() | ![]() | ![]() | ![]() |
Scatter | ![]() | ![]() | ![]() | ![]() | ![]() |
Granules | ![]() | ![]() | ![]() | ![]() | ![]() |
Washing resistance in °C |
40°C | 40°C | 40°C | 40°C | 40°C |
Fusing conditions with flow-through-press | |||||
Lamination temperature in °C | 90 - 95 | 80 - 85 | 75 - 82 | 75 - 82 | 70 - 75 |
Pneumatic pressure N / cm² | 2 - 4 | 2 - 4 | 2 - 4 | 2 - 4 | 2 - 4 |
Time in sec. | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 | 3 - 5 |
Appearance | White powder | White powder | White powder | White powder | White powder |
Type | Copolyester | LDPE | LDPE | LDPE |
Melting range / °C DSC | 110 - 115 | 102 - 106 | 100 - 104 | 98 - 102 |
Melting viscosity / g | ||||
MFI 160°C, 2.16 kg, 10 min. | 15 | |||
MFI 190°C, 2.16 kg, 10 min. | 40 | 70 | 150 | |
Chemical Basis | Copolyester | Low-Density-Polyethylene | Low-Density-Polyethylene | Low-Density-Polyethylene |
Powder sizes | ||||
Pastedot | ![]() | ![]() | ![]() | ![]() |
Doubledot | ![]() | ![]() | ![]() | ![]() |
Powderdot | ![]() | ![]() | ![]() | ![]() |
Scatter | ![]() | ![]() | ![]() | ![]() |
Granules | ![]() | ![]() | ![]() | ![]() |
Washing resistance in °C |
60°C | 60°C | 60°C | 40°C |
Fusing conditions with flow-through-press | ||||
Lamination temperature in °C | 130 - 150 | 130 - 150 | 130 - 140 | 120 - 130 |
Pneumatic pressure N / cm² | 3 - 10 | 3 - 5 | 3 - 5 | 2 - 5 |
Time in sec. | 12 - 20 | 10 - 15 | 10 - 15 | 8 - 10 |
Appearance | White powder | White powder | White powder | White |
Type | Copolyester | LDPE | LDPE | LDPE |
Melting range / °C DSC | 110 - 115 | 102 - 106 | 100 - 104 | 98 - 102 |
Melting viscosity / g | ||||
MFI 160°C, 2.16 kg, 10 min. | 15 | |||
MFI 190°C, 2.16 kg, 10 min. | 40 | 70 | 150 | |
Chemical Basis | Copolyester | Low-Density-Polyethylene | Low-Density-Polyethylene | Low-Density-Polyethylene |
Powder sizes | ||||
Pastedot | ![]() | ![]() | ![]() | ![]() |
Doubledot | ![]() | ![]() | ![]() | ![]() |
Powderdot | ![]() | ![]() | ![]() | ![]() |
Scatter | ![]() | ![]() | ![]() | ![]() |
Granules | ![]() | ![]() | ![]() | ![]() |
Washing resistance in °C |
60°C | 60°C | 60°C | 40°C |
Fusing conditions with flow-through-press | ||||
Lamination temperature in °C | 130 - 150 | 130 - 150 | 130 - 140 | 120 - 130 |
Pneumatic pressure N / cm² | 3 - 10 | 3 - 5 | 3 - 5 | 2 - 5 |
Time in sec. | 12 - 20 | 10 - 15 | 10 - 15 | 8 - 10 |
Appearance | White powder | White powder | White powder | White |
Type | TPU | TPU | TPU | TPU | TPU | TPU |
Melting range / °C DSC | 90 - 105 | 60 - 80 | 62 - 66 | - | 115 - 125 | - |
Melting viscosity / g | ||||||
MFI 160°C, 2.16 kg, 10 min. | 4 | 80 | 20 | 20 | 20 | 20 |
MFI 190°C, 2.16 kg, 10 min. | ||||||
Chemical Basis | Polyether PU | Polycaprolactone PU | Polycaprolactone PU | Aliphatic TPU | Aliphatic TPU | Aliphatic TPU |
Powder sizes | ||||||
Pastedot | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Doubledot | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Powderdot | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Scatter | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Granules | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Washing resistance in °C |
60°C | 60°C | 60°C | 60°C | 60°C | |
Fusing conditions with flow-through-press | ||||||
Lamination temperature in °C | 100 - 120 | 75 - 80 | 75 - 85 | 125 - 145 | 120 - 145 | 125 - 145 |
Pneumatic pressure N / cm² | 3 - 5 | 2 - 4 | 2 - 4 | 2 - 4 | 2 - 4 | 2 - 4 |
Time in sec. | 10 - 15 | 10 - 15 | 10 - 15 | 12 - 20 | 12 - 20 | 12 - 20 |
Appearance | White powder | White powder | White powder | White powder | White powder | white powder |
Type | TPU | TPU | TPU | TPU | TPU | TPU |
Melting range / °C DSC | 90 - 105 | 60 - 80 | 62 - 66 | - | 115 - 125 | - |
Melting viscosity / g | ||||||
MFI 160°C, 2.16 kg, 10 min. | 4 | 80 | 20 | 20 | 20 | 20 |
MFI 190°C, 2.16 kg, 10 min. | ||||||
Chemical Basis | Polyether PU | Polycaprolactone PU | Polycaprolactone PU | Aliphatic TPU | Aliphatic TPU | Aliphatic TPU |
Powder sizes | ||||||
Pastedot | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Doubledot | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Powderdot | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Scatter | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Granules | ![]() | ![]() | ![]() | ![]() | ![]() | ![]() |
Washing resistance in °C |
60°C | 60°C | 60°C | 60°C | 60°C | |
Fusing conditions with flow-through-press | ||||||
Lamination temperature in °C | 100 - 120 | 75 - 80 | 75 - 85 | 125 - 145 | 120 - 145 | 125 - 145 |
Pneumatic pressure N / cm² | 3 - 5 | 2 - 4 | 2 - 4 | 2 - 4 | 2 - 4 | 2 - 4 |
Time in sec. | 10 - 15 | 10 - 15 | 10 - 15 | 12 - 20 | 12 - 20 | 12 - 20 |
Appearance | White powder | White powder | White powder | White powder | White powder | white powder |