ROWAK AG

Mobiltech

The manufacturing of textile substrates for Mobiltech applications in terms of raw materials, construction, combination, functionality and recycling should be optimally aligned.

Increasing requirements for comfort and safety in cars/trucks result in a rising share of textiles in automotive applications. It ranges from rear shelves to seat covers and automotive wiring harness coverings. For composite constructions of trunk trims, rear shelves and floor units, mostly thermoplastic powders are used. Textile components in form of knitted or nonwoven distance fabrics invisibly provide a more comfortable seat-physiology in the seat construction.

New applications with textile components are absorbent nonwovens in batteries or fiber-optics in textile liners to illuminate specific areas (foot space, recessed grips, head/side liner) of the vehicle interior. Textiles and textilebased composites take over more functionalities in areas of shock absorption, acoustic insulation or heat protection.

 
Type CopolyamideCopolyamideCopolyamideCopolyamideCopolyamideCopolyamideCopolyamide
Melting range / °C DSC 120 - 13085 - 95105 - 115120 - 130110 - 120105 - 125100 - 120
Melting viscosity / g
MFI 160°C, 2.16 kg, 10 min. 1970202321040180
Chemical Basis CopolyamideCopolyamideCopolyamideCoPA/CopES BlendCopolyamideCopolyamideCopolyamide
Powder sizes
Pastedot
Doubledot
Powderdot
Scatter
Granules
Heat resistance
in °C
115801001101506090
Fusing conditions with flow-through-press
Lamination temperature in °C 140 - 16095 - 125120 - 140130 - 150120 - 140130 - 150110 - 145
Pneumatic pressure N / cm² 3 - 53 - 53 - 53 - 53 - 53 - 53 - 5
Time in sec. 12 - 2010 - 1510 - 1512 - 2010 - 1510 - 1510 - 15
Appearance White powderWhite powderWhite powderWhite powderwhite powderWhite powderWhite powder
 
Type CopolyamideCopolyamideCopolyamideCopolyamideCopolyamideCopolyamideCopolyamide
Melting range / °C DSC 120 - 13085 - 95105 - 115120 - 130110 - 120105 - 125100 - 120
Melting viscosity / g
MFI 160°C, 2.16 kg, 10 min. 1970202321040180
Chemical Basis CopolyamideCopolyamideCopolyamideCoPA/CopES BlendCopolyamideCopolyamideCopolyamide
Powder sizes
Pastedot
Doubledot
Powderdot
Scatter
Granules
Heat resistance
in °C
115801001101506090
Fusing conditions with flow-through-press
Lamination temperature in °C 140 - 16095 - 125120 - 140130 - 150120 - 140130 - 150110 - 145
Pneumatic pressure N / cm² 3 - 53 - 53 - 53 - 53 - 53 - 53 - 5
Time in sec. 12 - 2010 - 1510 - 1512 - 2010 - 1510 - 1510 - 15
Appearance White powderWhite powderWhite powderWhite powderwhite powderWhite powderWhite powder
 
Type CopolyesterCopolyesterCopolyesterCopolyester
Melting range / °C DSC 118 - 123115 - 123118 - 125177 - 186
Melting viscosity / g
MFI 160°C, 2.16 kg, 10 min. 303535
Chemical Basis CopolyesterCopolyesterCopolyesterCopolyester
Powder sizes
Pastedot
Doubledot
Powderdot
Scatter
Granules
Heat resistance
in °C
100100100140
Fusing conditions with flow-through-press
Lamination temperature in °C 130 - 150125 - 145125 - 145210 - 230
Pneumatic pressure N / cm² 3 - 52 - 53 - 53 - 10
Time in sec. 10 - 1210 - 1512 - 2012 - 20
Appearance White powderWhite powderWhite powderWhite powder
 
Type CopolyesterCopolyesterCopolyesterCopolyester
Melting range / °C DSC 118 - 123115 - 123118 - 125177 - 186
Melting viscosity / g
MFI 160°C, 2.16 kg, 10 min. 303535
Chemical Basis CopolyesterCopolyesterCopolyesterCopolyester
Powder sizes
Pastedot
Doubledot
Powderdot
Scatter
Granules
Heat resistance
in °C
100100100140
Fusing conditions with flow-through-press
Lamination temperature in °C 130 - 150125 - 145125 - 145210 - 230
Pneumatic pressure N / cm² 3 - 52 - 53 - 53 - 10
Time in sec. 10 - 1210 - 1512 - 2012 - 20
Appearance White powderWhite powderWhite powderWhite powder
 
Type TPUTPUTPUTPUTPUTPUTPU
Melting range / °C DSC 90 - 10560 - 8080 - 8562 - 66130 - 145115 - 125 -
Melting viscosity / g
MFI 160°C, 2.16 kg, 10 min. 4804520402020
MFI 190°C, 2.16 kg, 10 min.
Chemical Basis Polyether PUPolycaprolactone PUEco TPUPolycaprolactone PUAromatic Polyester PUAliphatic TPUAliphatic TPU
Density 1.21.191.191.191.19
Powder sizes
Pastedot
Doubledot
Powderdot
Scatter
Granules
Heat resistance
in °C
90701109090
Fusing conditions with flow-through-press
Lamination temperature in °C 100 - 12075 - 8090 - 10075 - 85135 - 150120 - 145125 - 145
Pneumatic pressure N / cm² 3 - 52 - 42 - 42 - 43 - 52 - 42 - 4
Time in sec. 10 - 1510 - 1510 - 1510 - 1512 - 2012 - 2012 - 20
Appearance White powderWhite powderWhite powderWhite powderWhite powderWhite powderWhite powder
 
Type TPUTPUTPUTPUTPUTPUTPU
Melting range / °C DSC 90 - 10560 - 8080 - 8562 - 66130 - 145115 - 125 -
Melting viscosity / g
MFI 160°C, 2.16 kg, 10 min. 4804520402020
MFI 190°C, 2.16 kg, 10 min.
Chemical Basis Polyether PUPolycaprolactone PUEco TPUPolycaprolactone PUAromatic Polyester PUAliphatic TPUAliphatic TPU
Density 1.21.191.191.191.19
Powder sizes
Pastedot
Doubledot
Powderdot
Scatter
Granules
Heat resistance
in °C
90701109090
Fusing conditions with flow-through-press
Lamination temperature in °C 100 - 12075 - 8090 - 10075 - 85135 - 150120 - 145125 - 145
Pneumatic pressure N / cm² 3 - 52 - 42 - 42 - 43 - 52 - 42 - 4
Time in sec. 10 - 1510 - 1510 - 1510 - 1512 - 2012 - 2012 - 20
Appearance White powderWhite powderWhite powderWhite powderWhite powderWhite powderWhite powder
 
Type LDPELDPELDPELDPELDPE
Melting range / °C DSC 107 - 110104 - 108102 - 106100 - 10498 - 102
Melting viscosity / g
MFI 190°C, 2.16 kg, 10 min. 8204070150
Chemical Basis Low-Density-PolyethyleneLow-Density-PolyethyleneLow-Density-PolyethyleneLow-Density-PolyethyleneLow-Density-Polyethylene
Density 0.920.9180.9170.9180.916
Powder sizes
Pastedot
Doubledot
Powderdot
Scatter
Granules
Washing resistance
in °C
60°C60°C60°C60°C40°C
Heat resistance
in °C
8080808060
Fusing conditions with flow-through-press
Lamination temperature in °C 130 - 150130 - 150130 - 150130 - 140120 - 130
Pneumatic pressure N / cm² 3 - 53 - 53 - 53 - 52 - 5
Time in sec. 10 - 1510 - 1510 - 1510 - 158 - 10
Appearance White powderWhite powderWhite powderWhite powderWhite
 
Type LDPELDPELDPELDPELDPE
Melting range / °C DSC 107 - 110104 - 108102 - 106100 - 10498 - 102
Melting viscosity / g
MFI 190°C, 2.16 kg, 10 min. 8204070150
Chemical Basis Low-Density-PolyethyleneLow-Density-PolyethyleneLow-Density-PolyethyleneLow-Density-PolyethyleneLow-Density-Polyethylene
Density 0.920.9180.9170.9180.916
Powder sizes
Pastedot
Doubledot
Powderdot
Scatter
Granules
Washing resistance
in °C
60°C60°C60°C60°C40°C
Heat resistance
in °C
8080808060
Fusing conditions with flow-through-press
Lamination temperature in °C 130 - 150130 - 150130 - 150130 - 140120 - 130
Pneumatic pressure N / cm² 3 - 53 - 53 - 53 - 52 - 5
Time in sec. 10 - 1510 - 1510 - 1510 - 158 - 10
Appearance White powderWhite powderWhite powderWhite powderWhite
 
Type HDPEHDPEHDPE
Melting range / °C DSC 130 - 135128 - 130125 - 128
Melting viscosity / g
MFI 190°C, 2.16 kg, 10 min. 4620
Chemical Basis High-Density-PolyethyleneHigh-Density-PolyethyleneHigh-Density-Polyethylene
Density 0.9440.960.956
Powder sizes
Pastedot
Doubledot
Powderdot
Scatter
Granules
Heat resistance
in °C
110110110
Fusing conditions with flow-through-press
Lamination temperature in °C 170 - 180155 - 170150 - 170
Pneumatic pressure N / cm² 15 - 2510 - 2010 - 20
Time in sec. 12 - 1812 - 1810 - 12
Appearance White powderWhite powderWhite powder
 
Type HDPEHDPEHDPE
Melting range / °C DSC 130 - 135128 - 130125 - 128
Melting viscosity / g
MFI 190°C, 2.16 kg, 10 min. 4620
Chemical Basis High-Density-PolyethyleneHigh-Density-PolyethyleneHigh-Density-Polyethylene
Density 0.9440.960.956
Powder sizes
Pastedot
Doubledot
Powderdot
Scatter
Granules
Heat resistance
in °C
110110110
Fusing conditions with flow-through-press
Lamination temperature in °C 170 - 180155 - 170150 - 170
Pneumatic pressure N / cm² 15 - 2510 - 2010 - 20
Time in sec. 12 - 1812 - 1810 - 12
Appearance White powderWhite powderWhite powder
 
Type EVAFlame retardant powderIonomer
Melting range / °C DSC 59 - 65110 - 12095 - 100
Melting viscosity / g
MFI 190°C, 2.16 kg, 10 min. 456
Chemical Basis Ethylene-Vinyl-AcetateCopolymer BlendIonomer / Copolymer
Density 0.9560.94
VA-Content (%) 33%
Powder sizes
Pastedot
Doubledot
Powderdot
Scatter
Granules
Heat resistance
in °C
409580
Fusing conditions with flow-through-press
Lamination temperature in °C 75 - 82 - -
Pneumatic pressure N / cm² 2 - 4 - -
Time in sec. 3 - 5 - -
Appearance White powderWhite, weak odouros PowderWhite powder
 
Type EVAFlame retardant powderIonomer
Melting range / °C DSC 59 - 65110 - 12095 - 100
Melting viscosity / g
MFI 190°C, 2.16 kg, 10 min. 456
Chemical Basis Ethylene-Vinyl-AcetateCopolymer BlendIonomer / Copolymer
Density 0.9560.94
VA-Content (%) 33%
Powder sizes
Pastedot
Doubledot
Powderdot
Scatter
Granules
Heat resistance
in °C
409580
Fusing conditions with flow-through-press
Lamination temperature in °C 75 - 82 - -
Pneumatic pressure N / cm² 2 - 4 - -
Time in sec. 3 - 5 - -
Appearance White powderWhite, weak odouros PowderWhite powder
Competence in Bonding Technologies
ROWAK AG

Rowalit Hotmelt Adhesives / Rowaflex Additives

DE