Buildtech is a synonym for all important and innovations in membrane-, light- and solid construction as well as for earthwork-, water- and road building.

In this segment textiles are applied in ie. concrete armouring, front-building systems, interior work, isolations, waterproof materials, noise prevention or sun protection. Textile substrates in composite materials in roof constructions are bonded with thermoplastic adhesive powders. A combination of high-rigid PES-fabric and laminar coated PTFE can be found in airports, hotels or stadiums.

Product name Type Melting range Melt Flow Index Powder sizes Resistance to dry cleaning Hand iron Enzyme washing Washing resistance Steam resistance Stone-wash resistance Heat resistance Fusing conditions with flow-through-press Appearance
Pastedot Doubledot Powderdot Scatter Granules Lamination temperature Pneumatic pressure Time
ROWALIT® PBT 01-1 PBT 220 – 230 °C DSC 115 g / 10 Min. (MFI 230°C) 0 – 80 µm ✕ ✕ ✕ ✕ 160 °C 250 – 260 °C 3 – 5 N/cm² 10 – 12 Sek. White powder
ROWALIT® BIOPOW 4000 Biobased Products, Copolyester 100 – 120 °C DSC 1 g / 10 Min. (MFI 190°C) 0 – 80 µm 80 – 200 µm 0 – 200 µm 0 – 300 µm
100 – 500 µm 		✓ 130 – 150 °C 3 – 5 N/cm² 12 – 20 Sek. White powder
ROWALIT® 1009 Copolymer Blend 65 – 110 °C DSC 90 g / 10 Min. (MFI 190°C) ✕ ✕ ✕ 0 – 400 µm
0 – 500 µm 		✕ 70 °C 120 – 135 °C 2 – 5 N/cm² 8 – 10 Sek. White powder
ROWALIT® 1014 Copolymer Blend 65 – 110 °C DSC 40 g / 10 Min. (MFI 190°C) ✕ ✕ ✕ 0 – 400 µm
0 – 500 µm 		✕ 75 °C 120 – 135 °C 2 – 5 N/cm² 8 – 10 Sek. White powder
ROWALIT® FS-16 Flame-retardant Powders 110 – 120 °C DSC ✕ ✕ ✕ ✓ ✕ 95 °C
ROWALIT® H8 LDPE 107 – 110 °C DSC 8 g / 10 Min. (MFI 190°C) ✕ ✕ ✕ ✓ ✓ 60 °C 80 °C 130 – 150 °C 3 – 5 N/cm² 10 – 15 Sek. White powder
ROWALIT® SS 8 Ionomer 95 – 100 °C DSC 6 g / 10 Min. (MFI 190°C) ✕ ✕ ✕ ✓ ✕ 80 °C 130 – 150 °C 3 – 5 N/cm² 10 – 20 Sek.